Adiprene® LF 1600D
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | svPLuo_Adiprene-LF-1600D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADIPRENE® LF 1600D is a TDI-terminated polyester prepolymer having very low free TDI content. This prepolymer also has low viscosity, which allows it to be processed at reduced temperature for better heat stability and longer pot life. It yields a high performance, 60 Shore D hardness elastomer when cured with 4,4'-methylene-bis-(o-chloroaniline), commonly called MBCA. Features of ADIPRENE LF 1600D include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 to 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% Strain | 4.65 | MPa | |
| 10% Strain | 9.72 | MPa | |
| 15% Strain | 14.0 | MPa | |
| 20% Strain | 19.1 | MPa | |
| 25% Strain | 25.2 | MPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 80.6 | N/mm | ASTM D1938 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 19.3 | MPa | |
| 300% Strain | 34.5 | MPa | |
| Tensile Strength | 52.4 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 131 | kN/m | ASTM D624 |
| Split | 33 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 33 | % | ASTM D395B |
| Bayshore Resilience | 38 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 3.0 to 4.0 | min | |
| Demold Time | 30 | min |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (100°C) | 16 | hr |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF14-60 XE-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Excelprene® 55F | S&E Specialty Polymers, LLC | TPE | Excelprene® |
| Ebalta MG 815-1 / MG 815 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| LUBMER™ LS4140 | Mitsui Chemicals America, Inc. | HMWPE | LUBMER™ |
| ESTOPLAST XU 6100HSNN01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |