LG ASA LI968W
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sv7I89_LG-ASA-LI968W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Good Weatherability Application Window Profile, Siding, Rain Gutter |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2060 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20mm | > 6.0 | % | ASTM D638 |
| Fracture, 3.20mm | 25 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 3.20 mm) | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 39 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 39 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 180 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 86.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Cylinder Zone 1 Temp. | 190 - 200 | °C | |
| Cylinder Zone 2 Temp. | 200 - 220 | °C | |
| Cylinder Zone 3 Temp. | 210 - 230 | °C | |
| Cylinder Zone 4 Temp. | 210 - 230 | °C | |
| Adapter Temperature | 210 - 230 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 210 - 250 | °C |
| Extrusion instructions |
|---|
| Roll Stack Temperature - Top: 70 to 90 °CRoll Stack Temperature - Middle: 70 to 90 °CRoll Stack Temperature - Bottom: 70 to 100 °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULATEC® PEEK CF 30 MV 14 | A. Schulman Europe | PEEK | SCHULATEC® |
| WPP PP PPC2TF2HS-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Edistir® N 1910 | Versalis S.p.A. | PS (GPPS) | Edistir® |
| OMIKRON FMS 30 R NERO 808 | TECNOPOL | PP Copolymer | OMIKRON |
| Dryflex® SE 90A201 | ELASTO | TPE | Dryflex® |