Honeywell PCTFE P3000TR

Category:	PCTFE , Polychlorotrifluoroethylene
Manufacturer:	Honeywell
Trademark:	Honeywell PCTFE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	suGES7_Honeywell-PCTFE-P3000TR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PCTFE P-Series TR film is a PCTFE homopolymer, high performance barrier film for industrial and electronics applications. It provides outstanding water vapor barrier and excellent chemical resistance.

General Information
Features	Homopolymer Good chemical resistance Barrier resin
Uses	Electrical/Electronic Applications Industrial application
Forms	Films

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.10	g/cm³	ASTM D792

Films	Nominal Value	Unit	Test Method
secant modulus			ASTM D882
MD	1170	MPa	ASTM D882
TD	1170	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Fracture	51.7	MPa	ASTM D882
TD : Fracture	41.4	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	200	%	ASTM D882
TD : Fracture	250	%	ASTM D882
Water Vapor Transmission	0.093	g/m²/24 hr	ASTM E96

Thermal	Nominal Value	Unit	Test Method
Peak Crystallization Temperature (DSC)	211	°C	ASTM D3418

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	100	%	ASTM D2863

Optical	Nominal Value	Unit	Test Method
Haze	< 1.0	%	ASTM D1003

Additional Information
Yield: 4380 in²/lbTensile Strength @ Break, ASTM D 882, MD: 6000 to 9000 psiTensile Strength @ Break, ASTM D 882, TD: 4500 to 7500 psiElongation @ Break, ASTM 882, MD: 150 to 250%Elongation @ Break, ASTM 882, TD: 200 to 300%Secant Modulus, ASTM D 882, MD: 150000 to 190000 psiSecant Modulus, ASTM D 882, TD: 150000 to 190000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 375 g/milGraves Tear (initial), ASTM D 1004, TD: 275 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: +5 to +10% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: -5 to -10% shrinkageFlammability: Non-flammable

Additional Information

Yield: 4380 in²/lbTensile Strength @ Break, ASTM D 882, MD: 6000 to 9000 psiTensile Strength @ Break, ASTM D 882, TD: 4500 to 7500 psiElongation @ Break, ASTM 882, MD: 150 to 250%Elongation @ Break, ASTM 882, TD: 200 to 300%Secant Modulus, ASTM D 882, MD: 150000 to 190000 psiSecant Modulus, ASTM D 882, TD: 150000 to 190000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 375 g/milGraves Tear (initial), ASTM D 1004, TD: 275 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: +5 to +10% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: -5 to -10% shrinkageFlammability: Non-flammable

Resin Grade	Manufacturer	Category	Trademark
Silplus® 60 EX	Momentive Performance Materials Inc.	Silicone Rubber, HTV	Silplus®
BJB Polyurethane TC-962 A/B	BJB Enterprises, Inc.	TSU	BJB Polyurethane
Expandable PS F32MB	INEOS Styrenics International SA	PS (EPS)	Expandable PS
FM® 410	Cytec Industries Inc.	Epoxy	FM®
Paracril® P3350CC2	INSA	NBR	Paracril®