ALTECH® PP-B A 4920/100 MR20
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® PP-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | stZN3o_ALTECH-PP-B-A-4920-100-MR20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH® PP-B A 4920/100 MR20 is a Polypropylene Copolymer (PP Copolymer) product filled with 20% talc. It is available in Asia Pacific, Europe, or North America. Applications of ALTECH® PP-B A 4920/100 MR20 include automotive, construction applications and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 40.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 100 | % | ISO 527-2 |
| Flexural Modulus | 1850 | MPa | ISO 178 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 60.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Circulation Dryer | 80.0 to 120 | °C | |
| Desiccant Dryer | 80.0 to 120 | °C | |
| Drying Time | |||
| Circulation Dryer | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 200 to 270 | °C | |
| Mold Temperature | 20.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ NH4050 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| ACRYLITE® Satinice df21 8N | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| Honeywell PCTFE P10000HS | Honeywell | PCTFE | Honeywell PCTFE |
| Karina BLACK PVC COMPOUND 825-48/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYFORT® FPP 1239 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |