| P-90 is a high tear strength, platinum-catalyzed, RTV-2 silicone rubber. It is easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. Addition-cure two-component silicone rubbers exhibit excellent chemical and heat resistance, but may show inhibition sensitivity. P-90 offers excellent release properties and is extremely useful for those applications where exceptional flexibility and tear resistance are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 316 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.885 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 12 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 40000 to 55000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Red | ||
| -- 3 | White | ||
| Viscosity | |||
| -- 4 | 1.5 to 2.5 | Pa·s | |
| -- 5 | 60 to 80 | Pa·s | |
| Curing Time | 16 to 24 | hr | |
| Pot Life | 1.0 to 2.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 6 | 28 to 36 | ||
| Shore A 7 | 31 to 39 | ||
| Tensile Strength | 3.79 to 4.48 | MPa | ASTM D412 |
| Tensile Elongation at Break | 390 to 450 | % | ASTM D412 |
| Tear Strength | 20.1 to 23.6 | kN/m | ASTM D624 |
| Electric Strength | 23 | kV/mm | |
| Relative Permittivity (100 Hz) | 2.80 | ||
| Volume Resistivity | 5.0E+14 | ohms·cm | |
| Dissipation Factor (100 Hz) | 6.0E-3 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Activator |
| 3 . | Base |
| 4 . | Activator |
| 5 . | Base |
| 6 . | 1 Day |
| 7 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP M1500 | LG Chem Ltd. | PP Impact Copolymer | SEETEC PP |
| SOLLAMID B 2700 MW | Krisoll Resinas Plásticas Ltda. | Nylon 6 | SOLLAMID |
| NatureFlex™ 23NVS | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Axiall PVC 8803 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina BLUE PVC COMPOUND 650-06/127 (MP-1.0) (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |