Radel® R-5100

Category:	PPSU , Polyphenylsulfone
Manufacturer:	Solvay Specialty Polymers
Trademark:	Radel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	stTbeT_Radel-R-5100.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Radel® R-5100 is an opaque, general purpose polyphenylsulfone (PPSU) for injection molding, that offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins. This resin also offers a high deflection temperature and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties.

Black: Radel® R-5100 BK937

Bone: Radel® R-5100 NT15

Grey: Radel® R-5100 GY1137

Grey: Radel® R-5100 GY1037

Grey: Radel® R-5100 GY874

Red: Radel® R-5100 RD 1018

Orange: Radel® R-5100 OR1145

Yellow: Radel® R-5100 YL1337

Green: Radel® R-5100 GN1007

Blue: Radel® R-5100 BU1027

Violet: Radel® R-5100 VT2582

Brown: Radel® R-5100 BN1164

General Information
Filler / Reinforcement	Filler
Features	Acid Resistant Autoclave Sterilizable Base Resistant Biocompatible E-beam Sterilizable Ethylene Oxide Sterilizable Flame Retardant General Purpose Good Chemical Resistance Good Sterilizability Good Thermal Stability Heat Sterilizable High ESCR (Stress Crack Resist.) High Heat Resistance Hydrolytically Stable Radiation (Gamma) Resistant Radiation Sterilizable Radiotranslucent Steam Resistant Steam Sterilizable Ultra High Toughness
Uses	Aerospace Applications Aircraft Applications Connectors Dental Applications Food Service Applications Hospital Goods Medical Devices Medical/Healthcare Applications Plumbing Parts Surgical Instruments
Agency Ratings	FAA FAR 25.853a ISO 10993 3 NSF 51 4 NSF 61 5
RoHS Compliance	RoHS Compliant
Appearance	Black Colors Available Light Beige Opaque
Forms	Pellets
Processing Method	Blow Molding Extrusion Film Extrusion Injection Molding Machining Profile Extrusion Sheet Extrusion Thermoforming
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.30	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)	14 to 20	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.70	%	ASTM D955
Water Absorption (24 hr)	0.37	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2340	MPa	ASTM D638
Tensile Strength			ASTM D638
Yield	69.6	MPa
Break	69.6	MPa
Tensile Elongation			ASTM D638
Yield	7.2	%
Break	60	%
Flexural Modulus	2410	MPa	ASTM D790
Flexural Strength (Yield)	91.0	MPa	ASTM D790
Compressive Modulus	1730	MPa	ASTM D695
Compressive Strength	98.9	MPa	ASTM D695
Shear Strength	62.7	MPa	ASTM D732
Poisson's Ratio	0.42		ASTM E132

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	690	J/m	ASTM D256
Unnotched Izod Impact	No Break		ASTM D256
Tensile Impact Strength	399	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed	214	°C
1.8 MPa, Unannealed	207	°C
Glass Transition Temperature	220	°C	ASTM E1356
CLTE - Flow	5.6E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.35	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	9.0E+15	ohms·cm	ASTM D257
Dielectric Strength	14	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
60 Hz	3.44
1 kHz	3.40

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹(0.750 mm, ALL colors, UL file E36098)	V-0		UL 94
Oxygen Index	38	%	ASTM D2863

Optical	Nominal Value		Test Method
Refractive Index	1.672		ASTM D542

Injection	Nominal Value	Unit
Drying Temperature	149	°C
Drying Time	2.5	hr
Suggested Max Moisture	0.050	%
Rear Temperature	321	°C
Middle Temperature	349	°C
Front Temperature	349	°C
Processing (Melt) Temp	343 to 388	°C
Mold Temperature	138 to 163	°C
Back Pressure	0.345 to 0.689	MPa
Screw Compression Ratio	2.2:1.0

Note Message
1 .	These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions.

Resin Grade	Manufacturer	Category	Trademark
T-Blend® 5510N-PE	TSRC Corporation	TPE	T-Blend®
Adell Polyamide AJ-13	Adell Plastics, Inc.	Nylon 66	Adell Polyamide
ExxonMobil™ PP7143KNE1	ExxonMobil Chemical	PP Impact Copolymer	ExxonMobil™
KumhoSunny PC/ABS HAC8245	Shanghai KumhoSunny Plastics Co., Ltd.	PC+ABS	KumhoSunny PC/ABS
Kazan LLDPE PEENT07-7	Kazanorgsintez Joint Stock Company	LLDPE	Kazan LLDPE