Lucon® PS6070E
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | stEQoq_LuconPS6070E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Electrostatic Dissipation (1.0E+05 ~ 1.0E+07 ohm) Application Mobile Phone Camera Module Tray |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 44.1 | MPa | ASTM D638 |
| Flexural Modulus 2(3.20 mm) | 2940 | MPa | ASTM D790 |
| Flexural Strength 3(3.20 mm) | 76.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 87.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 - 1.0E+7 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 210 - 225 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 225 - 235 | °C | |
| Mold Temperature | 50 - 80 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3012 U | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Next Nylon 66 Prime Series PMS2-01S.GY. | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Axiall PVC 8778 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LCA® N66-80G33 Type | UniPlas, Inc. | Nylon 66 | LCA® |
| FUDOWLITE® F5760F | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |