Diamond ASA C1030
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Diamond ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | st1ioV_Diamond-ASA-C1030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diamond ASA C1030 is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by extrusion or injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(220°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 45.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 30 | % | ASTM D638 |
| Flexural Modulus - Tangent 4(3.18 mm, 50.8 mm Span) | 1970 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm, Injection Molded | 81.1 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 67.8 | °C | |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 5 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 232 to 260 | °C | |
| Front Temperature | 235 to 260 | °C | |
| Nozzle Temperature | 220 to 260 | °C | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.517 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Method I (3 point load), 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF33-66 XE-BKDX9 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Bergamid™ A70 MI40 H NC017 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Arlon® 1263 | Greene, Tweed & Co. | PEEK | Arlon® |
| LEXAN™ EXL1444 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ LUBRICOMP™ KN001 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |