RheTech Polypropylene FRG220-773UV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ssZ3hh_RheTech-Polypropylene-FRG220-773UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass Fiber Reinforced, Chemically Coupled, Flame Retardant,UV Stabilized, Polypropylene Copolymer, Pantone Q716-1-5 Light Grey, UL94 V-1. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 55.8 | MPa | ASTM D638 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 96 | J/m | ASTM D256 |
| Dart Drop Impact | 0.791 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 156 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 139 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 51.7 - 65.6 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 191 - 199 | °C | |
| Middle Temperature | 199 - 210 | °C | |
| Front Temperature | 199 - 210 | °C | |
| Nozzle Temperature | 204 - 210 | °C | |
| Mold Temperature | 23.9 - 37.8 | °C | |
| Injection Pressure | 2.76 - 8.27 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 2.07 - 6.89 | MPa | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 25 - 75 | rpm |
| Injection instructions |
|---|
| Injection Speed: Slow to Moderate, 0.5 to 1.0 in/minScrew RPM: Screw recovery 3 seconds before mold opens; 25-75 rpmCycle Time: Variable - wall thickness dependent |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® HX10 | A. Schulman Europe | ABS | RONFALIN® |
| GPPC ABS D-450 | GPPC Chemical Co., Ltd. | ABS | GPPC ABS |
| Iupiace® TX903B | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Karina WHITE PVC COMPOUND 800-10/61-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 08218 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |