SABIC® PP RA1E10
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ssCwmT_SABIC-PP-RA1E10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This random copolymer has a high molecular weight and therefore mainly used for extrusion. It is typically used in sheet extrusion. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.895 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 | |
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1000 | MPa | ASTM D638 |
| -- | 950 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 28.0 | MPa | ASTM D638 |
| Yield | 29.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 13 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | > 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256A |
| 23°C | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 128 | °C | ASTM D1525, ISO 306/A120 4 4 |
| -- | 67.0 | °C | ASTM D1525, ISO 306/B120 5 5 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 TC-C-30 FR | RTP Company | PPS | RTP |
| Di-Pak™ R-4545/30 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Grilamid® L 25 W 40 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| OPTUM® DPP30WF08AL | Ferro Corporation | Polyolefin, Unspecified | OPTUM® |
| PLUSTEK PA840G3 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |