Ultramid® T KR 4340 G6
| Category: | Nylon 6/6T , Polyamide 6/6T Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | srFomS_Ultramid-T-KR-4340-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Partially aromatic polyamid, halogen-free flame-retardant, light colorable, outstanding flame retardance, resistant to soldering temperatures |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (325°C/5.0 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.3 to 5.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.4 to 1.8 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 120 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.10 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 11000 | 11000 | MPa | ISO 178 |
| Flexural Stress | 240 | 210 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 8.5 | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | -- | kJ/m² | |
| 23°C | 65 | 50 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/A |
| Melting Temperature | 290 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 to 2.5E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 6.5E-5 to 7.5E-5 | -- | cm/cm/°C | |
| Specific Heat | 1200 | -- | J/kg/°C | |
| Thermal Conductivity | 0.37 | -- | W/m/K | DIN 52612 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.90 | 4.10 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | 0.027 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 310 to 330 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 320°C (unreinforced) or 330°C (reinforced), TW = 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MELOPAS® MF 2010 | RASCHIG GmbH | Mel Formald | MELOPAS® |
| WELLAMID Nylon 6000/51 GV 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| ADDINYL PMD 20170 | ADDIPLAST | Nylon 66 | ADDINYL |
| Axpoly® r-PS01 1064 | Axion Polymers | PS (HIPS) | Axpoly® |
| Kepital® F10-01 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |