Order Products : sales@su-jiao.com
ISPLEN® PM 360 AT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | srColy_ISPLEN-PM-360-AT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer, 30% mineral fillers reinforced and high melt flow rate. ISPLEN PM370 AV gives a good compromise between stiffness and impact strength, a low warpage and shrinkage behaviour. This product is high heat stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.60 to 0.90 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 32.0 | MPa | |
| Break | 24.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 19 | % | |
| Flexural Modulus | 3700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 1.6 | kJ/m² | |
| 0°C | 1.7 | kJ/m² | |
| 23°C | 2.3 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -20°C | 10 | kJ/m² | |
| 0°C | 12 | kJ/m² | |
| 23°C | 23 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 119 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 69.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A120 |
| -- | 100 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMTOPP BTP23 | Inteplast Group | PP, Unspecified | AMTOPP |
| Hostacom TRC 364N C12752 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| Mafill® CR H 1044 | Ravago Group | PP Homopolymer | Mafill® |
| CONTINUUM™ DMDE-6620 NT 7 BIMODAL | The Dow Chemical Company | HDPE | CONTINUUM™ |