KPOL-PP K-PPC 16.0

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	srCmMq_KPOL-PP-K-PPC-16-0.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Heterophasic Copolymer

Applications

Injection Molding, Automobile Applications, Battery case ; Base resin for compounding, high impact resistance parts.

Good stiffness parts; Injection with good mechanical strength ; Household; Toys ; Industrial Pails for Electronic.

Characteristics

The KPOL® resin is a propylene impact copolymer designed for injection molding applications, has excellent toughness and good dimensional stabilityIt is a controlled rheology grade.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant Controlled Rheology Food Contact Acceptable Good Dimensional Stability Good Stiffness Good Toughness High Impact Resistance Impact Copolymer Nucleated
Uses	Automotive Applications Battery Cases Compounding Household Goods Industrial Applications Pails Toys
Agency Ratings	FDA 21 CFR 177.1520
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	16	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	95		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	27.0	MPa	ASTM D638
Tensile Elongation ²(Break)	6.0	%	ASTM D638
Flexural Modulus - 1% Secant	1300	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	90	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	110	°C	ASTM D648
Vicat Softening Temperature	150	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
TAIRIPRO F2003	Formosa Plastics Corporation	PP Homopolymer	TAIRIPRO
Ultradur® B 4040 G11 HMG BK15029	BASF Corporation	PBT	Ultradur®
Nylex™ 4032	Multibase, A Dow Corning Company	Nylon+PP	Nylex™
Ekalon® 20 E I S CF 10	Sattler KunststoffWerk GmbH	PC	Ekalon®
Osterlene® MI-13-1.4	Osterman & Company	PS (MIPS)	Osterlene®