VICTREX® HT™ 22CA30
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® HT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sqzDmc_VICTREX-HT-22CA30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, colour black. Higher temperature applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Spiral Flow | 8.00 | cm | Internal method |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Vertical flow direction : 200°C | 0.70 | % | ISO 294-4 |
| Flow direction : 200°C | 0.10 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.050 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 26000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 260 | MPa | ISO 527-2 |
| Fracture, 125°C | 170 | MPa | ISO 527-2 |
| Fracture, 175°C | 110 | MPa | ISO 527-2 |
| Fracture, 225°C | 80.0 | MPa | ISO 527-2 |
| Fracture, 275°C | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.6 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 23000 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 370 | MPa | ISO 178 |
| 125°C | 240 | MPa | ISO 178 |
| 175°C | 170 | MPa | ISO 178 |
| 275°C | 90.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 300 | MPa | ISO 604 |
| 120°C | 210 | MPa | ISO 604 |
| 200°C | 95.0 | MPa | ISO 604 |
| 250°C | 65.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 8.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 368 | °C | ISO 75-2/A |
| Glass Transition Temperature | 152 | °C | ISO 11357-2 |
| Melting Temperature | 373 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : > 152°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : < 152°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 152°C | 3.5E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 152°C | 9.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.95 | W/m/K | ISO 22007-4 |
| Specific Heat Capacity (23°C) | 1800 | J/kg/°C | DSC |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Toxicity | NES 713 | ||
| CO content | 0.0500 | NES 713 | |
| CO2 content | 0.120 | NES 713 | |
| Total gases | 0.170 | NES 713 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 2(23°C) | 1.0E+5 | ohms·cm | ASTM D4496 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 550 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 380 | °C | |
| Middle Temperature | 390 - 395 | °C | |
| Front Temperature | 400 | °C | |
| Nozzle Temperature | 405 | °C | |
| Mold Temperature | 190 - 215 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | 405°C nozzle |
| 2 . | 1V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Terblend® N NG-02 UV | INEOS Styrolution Group GmbH | ABS+Nylon | Terblend® N |
| APEX® 80855 | Teknor Apex Company | PVC, Flexible | APEX® |
| Estaloc® 59104 RETPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estaloc® |
| SABIC® LLDPE 218BJ | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Badatron® PPS GF30 | Bada AG | PPS | Badatron® |