PRE-ELEC® PP 1393
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sqqyyX_PRE-ELEC-PP-1393.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PP 1393 is a conductive thermoplastic concentrate based on polypropylene. Conductivity is achieved by using special conductive carbon black. PRE-ELEC® PP 1393 contains a high load of carbon black and it can be diluted up to 50% with virgin or recycled PP. The actual amount should always be tested as it also depends on the processing conditions. PRE-ELEC® PP 1393 is developed especially for extrusion of corrugated board. It can be also used for solid sheets and profiles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 0.50 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.3 - 1.6 | % | ASTM D955 |
| Flow direction | 1.3 - 1.6 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 97 | ASTM D2240, ISO 868 | |
| Shaw D | 71 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 15 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1520 | MPa | ASTM D790 |
| 4.00 mm | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 4.2 | kJ/m² | ASTM D256 |
| -20°C | 6.0 | kJ/m² | ISO 179 |
| 23°C | 8.0 | kJ/m² | ISO 179 |
| 23°C | 6.3 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 6.30 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 18.9 | kJ/m² | ASTM D256 |
| Notched Izod Impact 3 | ISO 180 | ||
| -20°C | 8.0 | kJ/m² | ISO 180 |
| 23°C | 19 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 87.2 | °C | ASTM D648B |
| 0.45 MPa, not annealed | 87.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 52.8 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 86.1 | °C | ASTM D1525 5 |
| -- | 152 | °C | ASTM D1525, ISO 306/A50 4 6 |
| -- | 86.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+4 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 210 | °C | |
| Cylinder Zone 3 Temp. | 210 | °C | |
| Cylinder Zone 4 Temp. | 220 | °C | |
| Cylinder Zone 5 Temp. | 220 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 220°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2500 A HB | RTP Company | PC+ABS | RTP |
| Pro-fax SB786 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| StarCLEAR CLR-1050 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarCLEAR |
| Sup-tech A705H | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| Generic Nylon 66+Nylon 6I/X | Generic | Nylon 66+Nylon 6I/X | Generic |