Ultramid® B3WG6 GP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sqQke6_Ultramid-B3WG6-GP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre reinforced and heat ageing resistant injection moulding grade, with enhanced flowability used e.g. for automobile manifolds |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/10.0 kg) | 55.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.75 | -- | % | ISO 294-4 |
| Flow direction | 0.25 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.3 - 6.9 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 - 2.3 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 145 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.30 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Maximum operating temperature- short cycle operation | 200 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | -- | FMVSS 302 | |
| Polymer Abbreviation | PA6-GF30 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9600 | 5600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 165 | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.9 | 7.5 | % | ISO 527-2 |
| Flexural Modulus | 8700 | 5500 | MPa | ISO 178 |
| Flexural Stress | 260 | 160 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 90 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 16 | -- | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 280°C, TW = 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPC5GF2-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| ELASTOSIL® LR 3005/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| KOCETAL® GF706 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Hylon® N2007 | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Sylvin 5132-75 Clear Blue 8281 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |