Plexar® PX3243
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Plexar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | snn6bf_PlexarPX3243.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s). |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm, blown film | 11.8 | MPa | ASTM D882 |
| TD : Yield, 51 µm, blown film | 13.8 | MPa | ASTM D882 |
| MD : Broken, 51 µm, blown film | 22.9 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 2.10 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : yield, 51 µm, blow film | 12 | % | ASTM D882 |
| TD : yield, 51 µm, blow film | 9.0 | % | ASTM D882 |
| MD : Broken, 51 µm, blown film | 780 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 840 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm, blown film | 69 | g | ASTM D1922 |
| TD : 51 µm, blown film | 240 | g | ASTM D1922 |
| Water Vapor Transmission Rate (100% RH, 51 µm, Blown Film) | 52 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 103 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP TE5105 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| VESTAMID® HTplus M3035 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| Anjacom® 200C-UV | Almaak International GmbH | Nylon 6 | Anjacom® |
| BUP 690 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| Ferro PP LPP40BK09BK | Ferro Corporation | PP, Unspecified | Ferro PP |