Borealis PP HD204CF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | smhHBC_Borealis-PP-HD204CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HD204CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C, Injection Molded) | 1350 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | > 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 700 | MPa | |
| TD : 50 µm | 700 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm | 45.0 | MPa | |
| TD : 50 µm | 35.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 600 | % | |
| TD : Break, 50 µm | 700 | % | |
| Instrumented Dart Impact (50 µm) | 10.0 | J | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 162 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 120 | ASTM D2457 | |
| Haze (50.0 µm) | < 2.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S-1180 | Lubrizol Advanced Materials, Inc. | Acrylic, Unspecified | Stat-Rite® |
| Durez® 32962 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Globalene® PC366-5 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Globalene® ST611K | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| KRATON® G7820 GU-N | Kraton Polymers LLC | SEBS | KRATON® |