duoMatrix®-C is new polymer additive that enhances the physical and performance properties of cementitious materials such as portland cements and mortars. duoMatrix®-C (Matrix®-C for short) eliminates the need for the usual 7-day post cure. It drastically reduces water and salt absorption and fills in micro cracks to minimize crack propagation. Other performance characteristics include greatly enhanced freeze/thaw, ultra-violet, and chemical resistance. Higher flexural strength reduces brittleness. Matrix®-G is available to enhance the performance of alpha-gypsums. Matrix®-C is easy to use and can be introduced to any aggregate mix. It is usually cast solid or mixed with chopped fiber and sprayed. Matrix®-C can be pigmented and improves color uniformity. Matrix®-C will improve processing of GFRC, making architectural elements and concrete castings (ornamental, etc.) more durable. Mix Ratio for GFRC: Pre-Mix Type 1 Cement: 100 parts Sand: 80 parts Matrix® C: 15 parts Water: 23 parts A-R Glass: 6 parts Spray Up Type 1 Cement: 100 parts Sand: 100 parts Matrix® C: 15 parts Water: 23 parts A-R Glass: 10 parts

Message

duoMatrix®-C is new polymer additive that enhances the physical and performance properties of cementitious materials such as portland cements and mortars. duoMatrix®-C (Matrix®-C for short) eliminates the need for the usual 7-day post cure. It drastically reduces water and salt absorption and fills in micro cracks to minimize crack propagation. Other performance characteristics include greatly enhanced freeze/thaw, ultra-violet, and chemical resistance. Higher flexural strength reduces brittleness. Matrix®-G is available to enhance the performance of alpha-gypsums.

Matrix®-C is easy to use and can be introduced to any aggregate mix. It is usually cast solid or mixed with chopped fiber and sprayed.
Matrix®-C can be pigmented and improves color uniformity. Matrix®-C will improve processing of GFRC, making architectural elements and concrete castings (ornamental, etc.) more durable.

Mix Ratio for GFRC:
Pre-Mix
Type 1 Cement: 100 parts
Sand: 80 parts
Matrix® C: 15 parts
Water: 23 parts
A-R Glass: 6 parts

Spray Up
Type 1 Cement: 100 parts
Sand: 100 parts
Matrix® C: 15 parts
Water: 23 parts
A-R Glass: 10 parts

General Information
Features	Good Chemical Resistance Good Crack Resistance Good Flexibility Good UV Resistance Low to No Water Absorption Salt Water/Spray Resistant
Uses	Blending
Processing Method	Casting Spraying

Physical	Nominal Value	Unit
Specific Volume	1.060	g/cm³

Additional Information	Nominal Value	Unit
Freeze/Thaw Resistance	3.0E+2	Cycles
Permeability	1200 coulombs

Physical	Nominal Value	Unit
Density	1.60 to 2.08	g/cm³

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	< 6.21	MPa	ASTM D638
Flexural Strength	< 34.5	MPa	ASTM D790
Compressive Strength	< 89.6	MPa	ASTM D695

Thermoset	Nominal Value	Unit
Pot Life	45 to 90	min
Demold Time	960	min

Resin Grade	Manufacturer	Category	Trademark
YUNGSOX® PP 3504	Formosa Polypropylene	PP Impact Copolymer	YUNGSOX® PP
Chansieh Phenolic J-361-1	Chansieh Enterprises Co., LTD.	Phenolic	Chansieh Phenolic
Expandable PS F31B	INEOS Styrenics International SA	PS (EPS)	Expandable PS
HyTemp® AR12	Zeon Chemicals L.P.	Acrylic, Unspecified	HyTemp®
OTECH ALLOY OTO8550 - Riser Jacket	OTECH Corporation	TP, Unspecified	OTECH ALLOY