AKROMID® B3 F0 black 950089 (1813)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sm01uP_AKROMID-B3-F0-black-950089-1813-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 F0 black 950089 (1813) is a nonreinforced polyamide 6 with halogen- and phosphorusfree flame retardant, listed acc. UL 94 at 0,8 mm in all colours, meeting the demand high GWIT of the appliances industry. This material is listet at VDE. Application areas are housings, fasteners and cable connectors in the electro- and electronic industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.17 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.80 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.7 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4000 | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 77.0 | 42.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 3.5 | 22 | % | |
| Break | 12 | > 100 | % | |
| Flexural Modulus 1 | 3800 | 1280 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 kJ/m² | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 222 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Daicel PP PTS4N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| DOWLEX™ 2606 GC | The Dow Chemical Company | LLDPE | DOWLEX™ |
| FRblend® PC-1306 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC | FRblend® |
| Elastron® G G601.A45.N | Elastron USA, Inc. | SEBS | Elastron® G |
| KOPLA PA66 KDT1040 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |