Edgetek™ PK-30CF/000 EM BK
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | skv9xo_Edgetek-PK-30CF-000-EM-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek®The engineering thermoplastic polymer product portfolio includes a series of standard and customizable high-performance materials. The combination includes high-temperature resistant materials for high-temperature working environments, and high-modulus/structural materials for load-bearing, high-strength applications and flame-retardant products. These polymers are made by mixing engineering thermoplastic resins with different reinforcing additives, such as carbon fiber, glass fiber and glass beads. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.050 - 0.20 | % | ASTM D955 |
| Transverse flow | 1.4 - 1.6 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr, 3.18 mm | 0.050 | % | ASTM D570 |
| Saturation | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 89 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 25000 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Fracture, 23°C | 240 | MPa | ASTM D638 |
| Fracture, 120°C | 155 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 22000 | MPa | ASTM D790 |
| 120°C | 19000 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 370 | MPa | ASTM D790 |
| 120°C | 260 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 90 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 325 | °C | ASTM D648 |
| Glass Transition Temperature | 145 | °C | DSC |
| Melting Temperature (DSC) | 343 | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : < 146°C | 6.0E-6 | cm/cm/°C | ISO 11359-2 |
| Flow : > 146°C | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 146°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 146°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | ASTM E1461 | ||
| 60°C 4 | 0.48 | W/m/K | ASTM E1461 |
| 60°C 5 | 1.7 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+5 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 350 - 390 | °C | |
| Mold Temperature | 170 - 190 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| 4 . | through-plane |
| 5 . | in-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® SAN 1200-WC | Plastic Solutions, Inc. | SAN | PrimaFlex® |
| Catalyst CT/2-LR | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| FERREX® GPP40CC90UL | Ferro Corporation | PP Homopolymer | FERREX® |
| Halar® 558 | Solvay Specialty Polymers | ECTFE | Halar® |
| LG PMMA HI925HS | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |