Plexiglas® SG10

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Altuglas International of Arkema Inc.
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	skc0Gs_Plexiglas-SG10.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Plexiglas® SG10 is an impact modified acrylic resin suitable for injection molding and extrusion. This grade is formulated for approved medical applications. It is a high flow resin designed to provide outstanding light transmission and water white clarity for disposable medical applications.

Some of the features and benefits of Plexiglas® SG10 are:

Chemical Resistance

Good resistance to lipids and drug formulations

Good resistance to isopropyl alcohol (IPA)

Property retention after exposure to hospital antiseptics, acids and bases

Sterilization

Stable to gamma radiation, E-beam, and ETO

Rapid recovery with excellent color stability

Retention of transparency and clarity

Retention of mechanical properties

Durability and Processability

Moldflow simulation data available

Excellent melt processability

Reduced cycle times

Suitable for thin-wall applications and complex multi-cavity molds

Good bondability using solvent, ultrasonic, or radio frequency methods

General Information
Additive	Impact Modifier
Features	Alcohol Resistant Biocompatible Bondability BPA Free E-beam Sterilizable Ethylene Oxide Sterilizable Good Chemical Resistance Good Moldability High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Impact Modified Radiation (Gamma) Resistant
Uses	Medical Devices Medical/Healthcare Applications
Agency Ratings	ISO 10993 Part 4 ISO 10993 Part 5 USP Class VI
RoHS Compliance	RoHS Compliant
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.15	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	3.3	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.30 to 0.80	%	ASTM D955
Water Absorption (24 hr)	0.40	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	38		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1860	MPa	ASTM D638
Tensile Strength (Break)	36.5	MPa	ASTM D638
Tensile Elongation (Break)	50	%	ASTM D638
Flexural Modulus	1860	MPa	ASTM D790
Flexural Strength (Yield)	71.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	48	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load ¹			ASTM D648
0.45 MPa, Annealed	87.8	°C
1.8 MPa, Annealed	82.8	°C
Vicat Softening Temperature
--	93.0	°C	ASTM D1525 ²
--	80.0	°C	ASTM D1525 ³
Thermal Conductivity	0.22	W/m/K	ASTM C177

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Refractive Index ⁴	1.490		ASTM D542
Transmittance (3180 µm)	90.0	%	ASTM D1003
Haze (3180 µm)	< 2.0	%	ASTM D1003

Additional Information	Nominal Value		Test Method
ASTM Classification	PMMA 0230V2		ASTM D788

Note Message
1 .	Annealing cycle: 4hrs @ 176°F
2 .	Rate A (50°C/h), Loading 1 (10 N)
3 .	Rate A (50°C/h), Loading 2 (50 N)
4 .	ND @ 72°F

Resin Grade	Manufacturer	Category	Trademark
RheTech Polypropylene P261-01	RheTech, Inc.	PP Impact Copolymer	RheTech Polypropylene
TRIBIT® 1500GN20	Samyang Corporation	PBT	TRIBIT®
DAI-EL™ G-7329 (GN-34)	DAIKIN AMERICA, INC.	Fluorelastomer	DAI-EL™
Exelene® PP H0402	Montachem International, Inc.	PP Homopolymer	Exelene® PP
Karina IVORY PVC COMPOUND -E 818-35/ 1-Y-SN-ERM	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina