LONOY lonoy 3010
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Kingfa |
| Trademark: | LONOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | shufCw_LONOY-lonoy-3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LONOY lonoy 3010 is a polycarbonate polybutene terephthalate (PC PBT) material, which contains a glass fiber reinforced material. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of LONOY lonoy 3010 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 75.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 10 | % | ASTM D638 |
| Flexural Modulus 3 | 3600 | MPa | ASTM D790 |
| Flexural Strength 4 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 180 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 700 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 140 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 125 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 30 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 245 - 260 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Processing (Melt) Temp | 245 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 280°CInjection Speed: 60 to 100% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ebalta BIV Epoxy 800 / BIV 800 | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| ELASTOSIL® 4300 | Wacker Chemie AG | Silicone | ELASTOSIL® |
| LNP™ THERMOCOMP™ UF0069S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| POLYFORT® FPP 20 GFC LE K1400 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| Sylvin 8368-70DUV Black | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |