Celstran® PP-GF20-05 Black
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | shGTsp_CelstranPPGF2005Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer reinforced with 20weight percent long glass fibers. Low emission. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.(-0553 = Low emission grade) Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functionial/structural parts for automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 4700 | MPa | ISO 527-2/1A/1 |
| 80°C | 3400 | MPa | ISO 527-2/1A |
| Tensile Stress | |||
| Fracture | 84.0 | MPa | ISO 527-2/1A/5 |
| 80°C | 60.0 | MPa | ISO 527-2/1A |
| Tensile Strain | |||
| Fracture | 2.5 | % | ISO 527-2/1A/5 |
| Fracture, 80°C | 2.6 | % | ISO 527-2/1A |
| Flexural Modulus | ISO 178 | ||
| 23°C | 4500 | MPa | ISO 178 |
| 80°C | 3400 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 140 | MPa | ISO 178 |
| 80°C | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 56 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 159 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 - 230 | °C | |
| Middle Temperature | 230 - 240 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Nozzle Temperature | 240 - 250 | °C | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30 - 70 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 230 to 270°CZone 4 Temperature: 250°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PC 740/4.5 FR UV CC1320-08LG | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Durez® 4400 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| INEOS Wire & Cable BPD2070 | INEOS Olefins & Polymers Europe | LDPE | INEOS Wire & Cable |
| Jamplast Inj-07 ABS | Jamplast, Inc. | ABS | Jamplast |
| O'Tech OM 5522 | O'Tech Corporation | PVC, Unspecified | O'Tech |