Infino TK-2050HL
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sgotBE_InfinoTK2050HL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino TK-2050HL is a polycyclohexyldimethyl terephthalate (PCT) product, which contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: mirrors. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.77 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.54 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.56 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.56 | % | ISO 2577 |
| Traffic : 3.20mm | 0.54 | % | ISO 2577 |
| Ash Content | |||
| -- | 51 | % | ASTM D5630 |
| -- | 51 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 111 | ASTM D785 | |
| R scale | 111 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4060 | MPa | ASTM D638 |
| -- | 4100 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 58.8 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 58.8 | MPa | ASTM D638 |
| Fracture | 56.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 2.1 | % | ASTM D638 |
| Fracture | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 6080 | MPa | ASTM D790 |
| -- 6 | 5200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 90.2 | MPa | ASTM D790 |
| -- 8 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10(23°C) | 22 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 29 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 27 | J/m | ASTM D256 |
| 23°C 11 | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C, 3.18 mm | 250 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 200 | J/m | ASTM D256 |
| -5°C 12 | 16 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 250 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 250 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 202 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 202 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 to 3.0mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| 12 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michimid K4220 | API Polymers, Inc. | Nylon 66 | Michimid |
| AMTOPP VA18 | Inteplast Group | PP, Unspecified | AMTOPP |
| Huaxia Shenzhou PFA DS708-C | Shandong Huaxia Shenzhou New Material Co., Ltd. | PFA | Huaxia Shenzhou |
| Lapex A | LATI S.p.A. | PESU | Lapex |
| LNP™ THERMOTUF™ VX99809 compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ THERMOTUF™ |