LEXAN™ EXL6414 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sgiltv_LEXAN-EXL6414-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC-Siloxane copolymer with excellent processability. Impact modified, medium flow, extreme low temp. ductility. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.40 to 0.80 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1720 | MPa | ASTM D638 |
| -- | 2280 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.2 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Break 3 | 60.0 | MPa | ASTM D638 |
| Break | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.5 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 100 | % | ASTM D638 |
| Break | 88 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2000 | MPa | ASTM D790 |
| -- 7 | 2090 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 85.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 690 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 11 | 60 | kJ/m² | ISO 180/1A |
| 23°C 12 | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 3200 | J/m | ASTM D4812 |
| -30°C 13 | No Break | ISO 180/1U | |
| 23°C 14 | No Break | ISO 180/1U | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 61.0 | J | |
| 23°C, Total Energy | 62.1 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 136 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 15 | 136 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 16 | 122 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525, ISO 306/B50 11 17 |
| -- | 140 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.1E+17 | ohms | IEC 60093 |
| Volume Resistivity | 1.7E+17 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.69 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.4E-3 | IEC 60250 | |
| Arc Resistance 18 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Nozzle Temperature | 288 to 310 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*3 |
| 15 . | 120*10*4 mm |
| 16 . | 120*10*4 mm |
| 17 . | Rate B (120°C/h), Loading 2 (50 N) |
| 18 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICTREX® PEEK 151G | Victrex plc | PEEK | VICTREX® PEEK |
| NEALID XN093 - 8428 | AD majoris | Nylon, Unspecified | NEALID |
| DuPure® QW 76 AV | Ducor Petrochemicals BV | PP Random Copolymer | DuPure® |
| LG MABS TR530F | LG Chem Ltd. | MABS | LG MABS |
| LEXAN™ 943 resin | SABIC Innovative Plastics | PC | LEXAN™ |