LNP™ LUBRICOMP™ OCP36F compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sgaDRw_LNPLUBRICOMPOCP36Fcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* OCP36F is a compound based on PPS - Linear resin containing Bearing Grade, Carbon Fiber, Lubricants. Added features of this material include: Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound O-BG SM Product reorder name: OCP36F |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.10 - 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 18100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 158 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus | 19900 | MPa | ASTM D790 |
| Flexural Strength | 246 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.47 | ASTM D3702 Modified | |
| With Self-Static | 0.33 | ASTM D3702 Modified | |
| Wear Factor - Washer | 24.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 56 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 490 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ E223U | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| PRIME TPO M142E | Prime Polymer Co., Ltd. | PP Impact Copolymer | PRIME TPO |
| VITAMIDE® BS10NT6336 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Electrafil® J-1200/CF/10/VO/ND | Techmer Engineered Solutions | ABS | Electrafil® |
| LNP™ LUBRICOMP™ Cycoloy_C2801 compound | SABIC Innovative Plastics | PC+ABS | LNP™ LUBRICOMP™ |