Novalloy-E EG506
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sgPmrt_Novalloy-E-EG506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-E EG506 is an Acrylonitrile Butadiene Styrene (ABS) material filled with 30% glass fiber. It is available in Asia Pacific. Primary attribute of Novalloy-E EG506: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 67.0 | MPa | ISO 527-2 |
| Flexural Modulus | 7600 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Notched Izod Impact (23°C, 6.40 mm) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 97.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 93.0 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 210 to 220 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPTON™ 1001 | Kuraray Co., Ltd. | SEP | SEPTON™ |
| Sinvicomp SRP2606/2 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Moplen EP301G | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Chiao Fu PP PP212GM30 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |
| Karina IVORY PVC COMPOUND -E 854-35/ 1-D-IS(VS-90)/K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |