Daelim Po1y® VL0005
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sg5cXr_DaelimPo1yVL0005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®VL0005 is a metallocene linear low density polyethylene product,. It is available in Europe or Asia Pacific. Daelim Po1y®The application areas of VL0005 include packaging, movies, industrial applications, food contact applications and additives/masterbatches. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 22 µm, extruded film | 43.1 | MPa | ASTM D882 |
| TD : Fracture, 22 µm, extruded film | 32.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 22 µm, extruded film | 380 | % | ASTM D882 |
| TD : Fracture, 22 µm, extruded film | 600 | % | ASTM D882 |
| Dart Drop Impact (22 µm, cast film) | 350 | g | ASTM D1709B |
| Seal Initiation Temperature 1(22 µm, cast film) | 92.0 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 82.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 91.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45, 22.0 µm, cast film) | 110 | ASTM D2457 | |
| Haze (22.0 µm, cast film) | 0.50 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 | °C |
| Note Message | |
|---|---|
| 1 . | HGT, 2.8 kg, 0.5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas 420 | PlastxWorld Inc. | ABS | Veroplas |
| TOTAL Polyethylene XSene® HDPE BM 593 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Arnite® TV4 461 | DSM Engineering Plastics | PBT+PET | Arnite® |
| OmniLon™ PA6 GR33 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |
| LNP™ THERMOCOMP™ DF002FV compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |