Retpol® 3019 HS
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sfXODF_Retpol-3019-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXTRON 3019 HS is a 30% glass fibre reinforced coupled polypropylene compound. It is a medium flow injection moulding grade developed for components requiring high rigidity and high heat deflection temperatures with excellent creep resistance and good impact strength. It is stabilised to meet heat aging requirements of 21 days at 150°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 113 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 83 | ||
| Shore D, 15 sec, 3.00 mm | 77 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 96.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 5900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 680 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 159 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 150 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravaflex BR M CIS | Ravago Group | PBR, Med Cis | Ravaflex |
| Vi-Chem PVC V142-90 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| CALP 1440G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Escorene™ Ultra MV 02514 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Jianqiao PC/ABS | Shanghai Jianqiao Plastic Co., Ltd. | PC+ABS | Jianqiao |