CALIBRE™ 3503
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sexITg_CALIBRE-3503.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 3503 is a polycarbonate resin offering an excellent balance of impact resistance, heat distortion resistance and optical clarity with outstanding process ability for injection molding applications. CALIBRE 3503 contains mould release and UV stabilizer. Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 35 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 71.0 | MPa | ASTM D638 |
| Break | 71.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 110 | % | ASTM D638 |
| Break | 110 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2400 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 97.0 | MPa | ASTM D790 |
| -- 9 | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 1800 | J/m | ASTM D256 |
| 23°C | 69 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 141 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Annealed | 140 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 138 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50, ASTM D1525 10 |
| Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 | ||
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 11 | UL 94 | ||
| 1.00 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index 12 | IEC 60695-2-12 | ||
| 1.00 mm | 900 | °C | |
| 2.00 mm | 875 | °C | |
| 3.00 mm | 875 | °C | |
| Glow Wire Ignition Temperature 13 | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 775 | °C | |
| 3.00 mm | 775 | °C | |
| Oxygen Index 14 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| 6 . | Method I (3 point load), 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Method I (3 point load), 2.0 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Rate A (50°C/h), Loading 2 (50 N) |
| 11 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 12 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 13 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 14 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RFL4020 100 NAT 20002 | Radici Plastics | Nylon 66 | Radilon® |
| ASI POLYETHYLENE EVA | A. Schulman Inc. | PE, Unspecified | ASI POLYETHYLENE |
| DAI-EL™ G-7800BP | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Fainplast PVC GK 91 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LNP™ THERMOCOMP™ KF006XXC compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |