EMERGE™ PC/ABS 7710
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | seTeZI_EMERGE-PC-ABS-7710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/ABS 7710 Advanced Resin is a high impact, ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. It has superior processability for injection molding applications, excellent aesthetics and is available in custom colors. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.17 | g/cm³ | ASTM D792 |
| -- | 1.18 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 11 | g/10 min | ASTM D1238 |
| 260°C/2.16 kg | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 2620 | MPa | ASTM D638 |
| 4.00 mm, Injection Molded | 2560 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 60.0 | MPa | ASTM D638 |
| Yield, 4.00 mm, Injection Molded | 55.0 | MPa | ISO 527-2/50 |
| Break | 48.3 | MPa | ASTM D638 |
| Break, 3.20 mm, Injection Molded | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield | 3.8 | % | ASTM D638 |
| Yield, 4.00 mm, Injection Molded | 3.8 | % | ISO 527-2/50 |
| Break | 65 | % | ASTM D638 |
| Break, 4.00 mm, Injection Molded | 43 | % | ISO 527-2/50 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Injection Molded | 15 | kJ/m² | |
| 23°C, Injection Molded | 40 | kJ/m² | |
| Notched Izod Impact | |||
| -22°C | 440 | J/m | ASTM D256 |
| -18°C | 200 | J/m | ASTM D256 |
| 23°C | 480 | J/m | ASTM D256 |
| -30°C, Injection Molded | 14 | kJ/m² | ISO 180/A |
| 23°C, Injection Molded | 50 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.6 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 79.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ASTM D1525, ISO 306/A120 2 1 |
| -- | 94.0 | °C | ISO 306/B50 |
| CLTE | ASTM D696 | ||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.2E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.60 mm, in Oil | 26 | kV/mm | |
| 3.20 mm, in Oil | 18 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.86 | ||
| 1 MHz | 2.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.0E-3 | ||
| 1 MHz | 7.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 2.50 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm 3 | 925 | °C | |
| 2.00 mm 4 | 925 | °C | |
| 2.50 mm | 925 | °C | |
| 3.00 mm 5 | 950 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 3107 | Covestro - Polycarbonates | PC | Makrolon® |
| Zythane® 6075D | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| NYCOA Polyamide ASN 27 150 KNF | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Braskem PP C706-21NAHP | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| DOW™ Electrical & Telecommunications DFDA-1648 NT EXP1 | The Dow Chemical Company | TP, Unspecified | DOW™ Electrical & Telecommunications |