Smooth-Cast® ONYX® Fast
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Smooth-Cast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | se7zOY_Smooth-Cast-ONYX-Fast.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Smooth-Cast ONYX® is a mercury-free urethane resin that cures quickly at room temperature to a deep black, solid plastic. ONYX® offers the convenience of a 1A:1B by volume mix ratio and has a very low viscosity, so it is easy to mix and pour. ONYX® has an ultimate shore hardness of 80D and offers higher physical properties and higher heat resistance vs. other general purpose resins. Advantages that ONYX® offers over other resins; 1) if you desire a black casting, adding color pigment is not necessary, 2) cured plastic is ultra-black and darker than competitive black resins, 3) cured ONYX® plastic can be polished and buffed to a high gloss shine and 4) ONYX® offers higher heat resistance vs. competitive black resins, 5) unlike other black resins, ONYX®does not contain mercury and 6) ONYX® is less expensive vs. other black resins. Applications include reproducing sculpture, making prototypes and potting / encapsulation. Because ONYX® is a fast curing resin and becomes hard quickly, it is also great for doing fast cold cast bronze, brass, copper, nickel/silver, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D1475 |
| Specific Volume | 1.00 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (23°C) | 10.0 to 15.0 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 1.0 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ASTM D638 |
| Tensile Strength | 40.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 1700 | MPa | ASTM D790 |
| Flexural Strength | 57.1 | MPa | ASTM D790 |
| Compressive Modulus | 534 | MPa | ASTM D695 |
| Compressive Strength | 60.4 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 120, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Pot Life (23°C) | 2.5 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 100 | cP | ASTM D2393 |
| Post Cure Time (121°C) | 4.0 to 6.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P20B11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| Rescarb PC | Polimarky Spolka Jawna | PC | Rescarb |
| TAIRILAC AF3535 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Nypol® PA A3 G25 PRTA010 NR438 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Avalon 37 | Greene, Tweed & Co. | UHMWPE | Avalon |