Prime ABS Film-X 100
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Primex Plastics Corporation |
| Trademark: | Prime ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sdtUDH_Prime-ABS-Film-X-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Prime ABS Film-X is a Prime ABS substrate with a UV and chemical resistant film. It is available in high gloss with a good DOI or low gloss. Applications: Prime ABS Film-X has a wide variety of possible exterior applications from side pillars, spoilers, side molding. It is ideal for any exterior application requiring a very high gloss or dull finish with UV and chemical resistance. Processing: Thermoforming temperatures, mold temperatures, de-molding and mold shrink are about the same as ABS. However, the film side of the sheet should be exposed to a minimum amount of heat in the oven of the former. Finishing: Cutting or machining of this product may be done by sawing, drilling, grinding, sanding, punching and die cutting. High pressure water and laser cutting will also work. This product may be bonded by chemicals, mechanical screws and other type of fasteners as well as sonic welding. Minor surface repairs may be made with Dupont 7 or 3M glazing compound. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Colors can be matched to any solid color, metallic, pearlescents, and tinted clears. Patterns include brushed metals, organics and geometrics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1390 | MPa | ASTM D638 |
| Flexural Modulus (3.18 mm) | 1890 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 37.9 | MPa | |
| TD : Yield | 36.5 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 93.3 | °C | |
| 1.8 MPa, Unannealed | 81.7 | °C | |
| CLTE - Flow | 8.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1(2.70 mm) | HB | UL 94 | |
| Flammability (> 2.70 mm) | Pass | FMVSS 302 |
| Note Message | |
|---|---|
| 1 . | >2.7mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBN7052 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| Ultramid庐 B3UM4 | BASF Corporation | Nylon 6 | Ultramid® |
| FERREX® GPP20CK14HB-GY | Ferro Corporation | PP, Unspecified | FERREX® |
| FOZEAS® J9503J | Mitsubishi Chemical Performance Polymers, Inc. | PLA | FOZEAS® |
| StarPet® 8015-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarPet® |