RTP 303 S TFE 20
| Category: | PC , Polycarbonate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | scct46_RTP-303-S-TFE-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6890 | MPa | ASTM D638 |
| Tensile Strength | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 750 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 3mil/in.Tensile Elongation, ASTM D-638: 2-3% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 288 - 343 | °C | |
| Middle Temperature | 288 - 343 | °C | |
| Front Temperature | 288 - 343 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 415 | Wacker Chemie AG | Silicone | POWERSIL® |
| RTP EMI 1060.7 | RTP Company | PBT | RTP |
| CompaDur® 121 GK 20 black (030) | DimeLika Plast GmbH | PBT | CompaDur® |
| Grilamid® XE 4108 nat | EMS-GRIVORY | Nylon 6/12 | Grilamid® |
| Moplen HP562T | LyondellBasell Industries | PP Homopolymer | Moplen |