InnoClear™ OC-5080
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoClear™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sbdPWA_InnoClear-OC-5080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OC-5080 is a water clear, semi-flexible polyurethane elastomer formulated for hand-batch or vacuum assisted processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI OC-5080 is low viscosity and uses materials that have excellent U.V. resistant qualities. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.07 | g/cm³ | |
| Hardener | 1.07 | g/cm³ | |
| Base Resin | 1.07 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 35 Mix Ratio by Volume: 35 | ||
| Demold Time | 180 to 300 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.20 | Pa·s | |
| 25°C 2 | 0.75 | Pa·s | |
| 25°C 3 | 0.85 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 12 to 18 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 72 to 82 | ASTM D2240 | |
| Tensile Strength | 5.96 | MPa | ASTM D638 |
| Tensile Elongation at Break | 95 | % | ASTM D638 |
| Tear Strength | 10.5 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake MDPE EB171 | Westlake Chemical Corporation | MDPE | Westlake MDPE |
| Flexalloy® 9300-85 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Horda E8472 | Horda Cable Compounds | PE, Unspecified | Horda |
| Iupiace® GH10 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Sylvin 6253-78 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |