LNP™ THERMOCOMP™ PF00DS compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sbApLK_LNP-THERMOCOMP-PF00DS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* PF00DS is a compound based on PA6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound PF10013HS Product reorder name: PF00DS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 235 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19000 | MPa | ISO 178 |
| Flexural Stress | 335 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 100 mm Span) | 220 | °C | ISO 75-2/Ae |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROPRENE® 1 A90 M1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Vydyne® R513H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| BorPure™ RD208CF | Borealis AG | PP Random Copolymer | BorPure™ |
| COSMOPLENE® FC9412G | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Random Copolymer | COSMOPLENE® |
| EBAC® SP1802 | Westlake Chemical Corporation | EnBA | EBAC® |