Stat-Rite® E1150
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Stat-Rite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sagQwh_Stat-Rite-E1150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Rite® E1150 blend is a static dissipative thermoplastic polyurethane (TPU) alloy. Stat-Rite E1150 utilizes the patented Stat-Rite inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. Stat-Rite alloys retain uniform static dissipation properties even when injection molded or extruded. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 88 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 5.20 | MPa | |
| 300% Strain | 12.4 | MPa | |
| Tensile Strength (Break) | 32.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 760 | % | ASTM D412 |
| Tear Strength | 68.0 | kN/m | ASTM D624 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | ASTM D257 |
| Volume Resistivity | 4.0E+10 | ohms·cm | ASTM D257 |
| Static Decay 1 | |||
| +5000 V to 50 V | 1.3 | sec | |
| -5000 V to -50 V | 1.3 | sec |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content | Internal Method | ||
| Anions Cl- | 3.00 | mg/m² | |
| Anions NO3- | 0.0300 | mg/m² | |
| Anions PO4- | 24.0 | mg/m² | |
| Anions SO4- | 0.800 | mg/m² | |
| Cations Ca | 0.300 | mg/m² | |
| Cations K | 0.500 | mg/m² | |
| Cations Li | 0.0400 | mg/m² | |
| Cations Mg | 0.0600 | mg/m² | |
| Cations Na | 15.0 | mg/m² | |
| Outgassing | Internal Method | ||
| MMA | < 0.100 | ppm | |
| Styrene | < 0.100 | ppm | |
| Toluene | < 0.100 | ppm | |
| Total Organics | < 0.100 | ppm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 | °C | |
| Drying Time | 2.0 to 3.0 | hr |
| Note Message | |
|---|---|
| 1 . | FTMS-101C, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP11-289A15 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| SKYBOND® 8500 | Industrial Summit Technology Co. | API | SKYBOND® |
| Xuchuan XWB-3360 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| LTP ZC-1180 | Chengdu Letian Plastics Co., Ltd | PPS, Linear | LTP |
| Osterlene® PPH-12-.8 | Osterman & Company | PP Homopolymer | Osterlene® |