VICTREX® PAEK WG™ 101
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® PAEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sagP3o_VICTREX-PAEK-WG-101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, PolyArylEtherKetone (PAEK), reinforced with wear additives, semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black. WG101 does not contain polytetrafluoroethylene (PTFE) or other halogenated additives. Tribological applications with thin cross sections or long flow lengths, with higher strength and stiffness. Excellent wear resistance, very low coefficient of friction and low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.44 | g/cm³ | ISO 1183 |
| Spiral Flow | 13.5 | cm | |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Vertical flow direction | 0.50 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.040 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 19000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 180 | MPa | ISO 527-2 |
| Fracture, 125°C | 125 | MPa | ISO 527-2 |
| Fracture, 175°C | 85.0 | MPa | ISO 527-2 |
| Fracture, 225°C | 65.0 | MPa | ISO 527-2 |
| Fracture, 275°C | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.9 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 17000 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 280 | MPa | ISO 178 |
| 125°C | 220 | MPa | ISO 178 |
| 175°C | 140 | MPa | ISO 178 |
| 275°C | 70.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 230 | MPa | ISO 604 |
| 120°C | 160 | MPa | ISO 604 |
| 200°C | 65.0 | MPa | ISO 604 |
| 250°C | 45.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 5.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 343 | °C | ISO 75-2/Af |
| Glass Transition Temperature | 143 | °C | ISO 11357-2 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : < 143°C | 9.0E-6 | cm/cm/°C | ISO 11359-2 |
| Flow : > 143°C | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 1.3 | W/m/K | ISO 22007-4 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 3(23°C) | 1.0E+6 | ohms·cm | IEC 60093 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 350 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 370 | °C | |
| Middle Temperature | 375 - 380 | °C | |
| Front Temperature | 385 | °C | |
| Nozzle Temperature | 390 | °C | |
| Mold Temperature | 180 - 210 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | Crystalline |
| 2 . | 390°C nozzle, 200°C tool |
| 3 . | 1V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2920-67 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| FHR Polypropylene P6C6B-134 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Ecodear® V911X51 | Toray Resin Company | PLA | Ecodear® |
| EPO-TEK® OG133-8 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Kepamid® 1330GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |