Bormod™ BE961MO
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | saera8_Bormod-BE961MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BE961MO is a heterophasic copolymer. This grade is characterized by an optimum combination of high stiffness, low creep and very high impact strength. This grade uses Borealis Nucleation Technology (BNT) to increase productivity by cycle time reduction. BNT in combination with excellent stiffness and good flow properties creates a high potential for wall-thickness reduction. Products originating from this grade have very good demoulding properties, well-balanced mechanical properties, excellent dimension consistency with respect to different colors and good organoleptic properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.3 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -20°C, Total Penetration Energy | 40.0 | J | |
| 0°C, Total Penetration Energy | 35.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 92.0 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 260 | °C | |
| Mold Temperature | 10.0 to 30.0 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 20.0 to 50.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection molded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG5 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| Monprene® CP-19048 CLR | Teknor Apex Company | TPE | Monprene® |
| Moplen EP340K | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| AZDEL™ R301B01N | Azdel, Inc. | PP Alloy | AZDEL™ |
| 3M™ Dyneon™ PTFE Compound FB 01N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |