Stat-Rite® S-506
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Stat-Rite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | saIkL7_Stat-Rite-S-506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stat-Rite® S-506 is a static dissipative High-Impact Polystyrene alloy. Stat-Rite® S-506 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to enhance standard HIPS packaging sheet with a layer of clean, permanent ESD protection. Used as a skin layer, Stat-Rite® S-506 provides more consistent ESD protection than coatings and anti-stat. The Stat-Rite® skin will NOT wash off or deteriorate over time, providing reliable ESD protection for many years. FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1380 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 20.7 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 85 | % | ASTM D638 |
| Flexural Modulus 4 | 1380 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistance - 12% R.H. 6 | 1.0E+9 | ohms·cm | ESD S11.11 |
| Surface Resistivity - 50% R.H. 7 | 3.0E+9 | ohms/sq | ASTM D257 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Filler Content | IDP Alloy |
| Note Message | |
|---|---|
| 1 . | measured on a co-extruded ABA sheet of S506/HIPS/S506 in a 10/80/10 thickness ratio |
| 2 . | measured on a co-extruded ABA sheet of S506/HIPS/S506 in a 10/80/10 thickness ratio |
| 3 . | measured on a co-extruded ABA sheet of S506/HIPS/S506 in a 10/80/10 thickness ratio |
| 4 . | measured on a co-extruded ABA sheet of S506/HIPS/S506 in a 10/80/10 thickness ratio |
| 5 . | measured on a co-extruded ABA sheet of S506/HIPS/S506 in a 10/80/10 thickness ratio |
| 6 . | measured on a co-extruded ABA sheet of S506/HIPS/S506 in a 10/80/10 thickness ratio |
| 7 . | measured on a co-extruded ABA sheet of S506/HIPS/S506 in a 10/80/10 thickness ratio |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 1553L | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Delrin® FG500TL NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| KumhoSunny PET HEG3645 | Shanghai KumhoSunny Plastics Co., Ltd. | PET | KumhoSunny PET |
| Optix® CA-927 G | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |
| Monprene® MP-1500 | Teknor Apex Company | TPE | Monprene® |