LNP™ THERMOTUF™ MF0049I compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sYeuWU_LNP-THERMOTUF-MF0049I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOTUF MF0049I is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features include; Flame Retardant, Chemically Coupled. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.34 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 57.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4700 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 156 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.2E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC1F-4009U | Spartech Polycom | ABS | Spartech |
| ALTECH® PBT A 1000/100 | ALBIS PLASTIC GmbH | PBT | ALTECH® PBT |
| Karina GREEN COLOR CONCENTRATE -E 40/272-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ALCOM® PA66 910/1.1 CF40 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| LUVOCOM® 1106-8380/WT | LEHVOSS Group | PEI | LUVOCOM® |