NEFTEKHIM ABS 0646
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sYaM4n_NEFTEKHIM-ABS-0646.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS 0646 -is an easy flow, molding, heat resistant grade with impact strength and temperature resistance during the process. It is an indigenous due to low yellow index and color resistance; it can be used mainly for production automobile internals, (extruded profile, interior finish and etc.) and with corresponding coating for external parts such as grids and looking glasses. It is produced self-colored only, additives/ dye free. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.5 to 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 43.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | DIN 53453 |
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 1 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Deflection Temperature | 108 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Styrene 2 | 0.050 | % | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-1 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 60 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | Test Method: TU 2214-159-05766801-2011 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starglas GX061104 | Eurostar Engineering Plastics | PSU | Starglas |
| Ultraform® N 2640 Z2 UNC Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Huafon JF-P-6765 / JF-I-6722 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Karina MBPEB WHITE 1000/5035-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPH GF5030 PD2 | Polykemi AB | PP Homopolymer | POLYfill |