Generic PP Copolymer - Talc
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sXsbqZ_Generic-PP-Copolymer---Talc.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer - Talc This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.948 - 1.25 | g/cm³ | ASTM D792 |
| 23°C | 0.964 - 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.60 - 21 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.50 - 21 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 6.80 - 9.20 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.70 - 1.4 | % | ASTM D955 |
| Transverse flow : 23°C | 0.75 - 1.6 | % | ASTM D955 |
| 23°C | 0.88 - 1.2 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 - 0.050 | % | ASTM D570 |
| 23°C, 24 hr | 0.049 - 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 50 - 88 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 65 - 74 | ASTM D2240 | |
| 23°C | 62 - 72 | ISO 868 | |
| Ball Indentation Hardness | 30.0 - 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1000 - 2530 | MPa | ASTM D638 |
| 23°C | 1650 - 3150 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 16.0 - 35.0 | MPa | ASTM D638 |
| Yield, 23°C | 17.3 - 35.8 | MPa | ISO 527-2 |
| Fracture, 23°C | 13.0 - 18.2 | MPa | ASTM D638 |
| Fracture, 23°C | 14.9 - 25.6 | MPa | ISO 527-2 |
| 23°C | 20.1 - 30.7 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 7.6 | % | ASTM D638 |
| Yield, 23°C | 1.7 - 9.5 | % | ISO 527-2 |
| Fracture, 23°C | 3.0 - 100 | % | ASTM D638 |
| Fracture, 23°C | 2.8 - 52 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1350 - 2530 | MPa | ASTM D790 |
| 23°C | 1450 - 2830 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 20.0 - 48.0 | MPa | ASTM D790 |
| 23°C | 17.0 - 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 13 - 66 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 22 - 99 | J/m | ASTM D256 |
| 23°C | 2.8 - 8.3 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 350 - 860 | J/m | ASTM D256 |
| 23°C | 12 - 18 | kJ/m² | ISO 180 |
| Dart Drop Impact (23°C) | 0.946 - 4.76 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 0.791 - 22.9 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 99.8 - 132 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 52.0 - 136 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 56.7 - 70.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.8 - 66.1 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 75.0 - 152 | °C | ASTM D1525 |
| -- | 70.0 - 153 | °C | ISO 306 |
| CLTE - Flow | |||
| -- | 5.9E-5 - 8.1E-5 | cm/cm/°C | ASTM D696 |
| -- | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI | 50.0 - 115 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 596 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 99 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 550 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 550 - 755 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 72.5 - 87.8 | °C | |
| Drying Time | 1.5 - 3.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.054 | % | |
| Rear Temperature | 199 - 216 | °C | |
| Middle Temperature | 209 - 230 | °C | |
| Front Temperature | 215 - 225 | °C | |
| Nozzle Temperature | 214 - 222 | °C | |
| Processing (Melt) Temp | 209 - 245 | °C | |
| Mold Temperature | 29.4 - 65.9 | °C | |
| Injection Pressure | 5.31 - 101 | MPa | |
| Holding Pressure | 3.96 - 5.49 | MPa | |
| Back Pressure | 0.300 - 0.840 | MPa | |
| Screw Speed | 50 - 51 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer - TalcThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® PXA 10200 | Tekni-Films, a div of Tekni-Plex | Film, Copolyester/PCTFE | TEKNIFLEX® |
| SUMILITE® PVC VSS-1104 | Sumitomo Bakelite Co., Ltd. | PVC, Unspecified | SUMILITE® PVC |
| Cri-Line TFEP-920 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Pearlthane® D11H95S | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| Pinnacle PP 1335 Z | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |