Romiloy® 5240 GF 30
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sWtzgH_Romiloy-5240-GF-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®5240 GF 30 is a polybutylene terephthalate + ASA (PBT + ASA) material, and the filler is 30% glass fiber reinforced material. This product is available in Europe, and the processing method is injection molding. Romiloy®The main characteristics of 5240 GF 30 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.30 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7750 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 101 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.9 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 7070 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 141 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 166 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 167 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | < 260 | °C | |
| Mold Temperature | 75.0 - 100 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | < 1.00 | MPa | |
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Holding Pressure: moderate to high |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S CP300 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| TEKNIFLEX® VPA12200 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| Vi-Chem PVC VSR55D-80 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TYNEA 2700 | Tyne Plastics LLC. | Acetal (POM) Copolymer | TYNEA |
| LEXAN™ EXL1434 resin | SABIC Innovative Plastics | PC | LEXAN™ |