RTP 400 SI 2

Category: PS (GPPS) , General Purpose Polystyrene
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: sVxPSp_RTP-400-SI-2.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Silicone Lubricated
General Information
Additive
  • Silicone Lubricant (2%)
Features
  • Lubricated
RoHS Compliance
  • Contact Manufacturer
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.04g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.60%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Modulus 3100MPaASTM D638
Tensile Strength 46.9MPaASTM D638
Tensile Elongation (Yield)6.0 to 10%ASTM D638
Flexural Modulus 3310MPaASTM D790
Flexural Strength 82.7MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)27J/mASTM D256
Unnotched Izod Impact (3.20 mm)270J/mASTM D4812
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)82.2°CASTM D648
FlammabilityNominal ValueTest Method
Flame Rating (1.50 mm, ** Values per RTP Company testing.)HBUL 94
InjectionNominal ValueUnit
Drying Temperature 82.2°C
Drying Time 2.0hr
Processing (Melt) Temp 210 to 249°C
Mold Temperature 37.8 to 65.6°C
Injection Pressure 68.9 to 103MPa
Resin Grade Manufacturer Category Trademark
SABIC® PP CX03-81 Saudi Basic Industries Corporation (SABIC) PP Copolymer SABIC® PP
TRYCITE™ 1003U The Dow Chemical Company PS (GPPS) TRYCITE™
Karina GRAY PVC COMPOUND 800-18/233-A-ERYB (***) Karina Ind. e Com. de Plásticos Ltda PVC, Unspecified Karina
LUVOCOM® 1105-8432 Lehmann & Voss & Co. PEEK LUVOCOM®
Durez® 37066 SBHPP Phenolic Durez®