Generic Nylon 610 - Carbon Fiber
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sVngbZ_Generic-Nylon-610---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 610 - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 - 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.070 - 0.40 | % | ASTM D955 |
| Transverse flow : 23°C | 0.80 - 0.90 | % | ASTM D955 |
| 23°C | 0.11 - 0.80 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.10 - 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 8270 - 19900 | MPa | ASTM D638 |
| 23°C | 9550 - 19500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 128 - 233 | MPa | ASTM D638 |
| Fracture, 23°C | 117 - 236 | MPa | ASTM D638 |
| Fracture, 23°C | 126 - 243 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.8 - 3.5 | % | ASTM D638 |
| Fracture, 23°C | 1.9 - 3.0 | % | ASTM D638 |
| Fracture, 23°C | 1.6 - 2.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5990 - 16800 | MPa | ASTM D790 |
| 23°C | 6720 - 15400 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 172 - 294 | MPa | ASTM D790 |
| 23°C | 185 - 349 | MPa | ISO 178 |
| Coefficient of Friction | 0.27 - 0.47 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 - 110 | J/m | ASTM D256 |
| 23°C | 4.4 - 15 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 380 - 860 | J/m | ASTM D256 |
| 23°C | 29 - 68 | kJ/m² | ISO 180 |
| Multi-Axial Instrumented Impact Energy (23°C) | 1.24 - 9.39 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 218 - 222 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 211 - 218 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 193 - 216 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.8 - 82.5 | °C | |
| Drying Time | 4.0 - 4.1 | hr | |
| Suggested Max Moisture | 0.16 | % | |
| Rear Temperature | 254 - 255 | °C | |
| Middle Temperature | 265 - 266 | °C | |
| Front Temperature | 276 - 277 | °C | |
| Processing (Melt) Temp | 256 - 274 | °C | |
| Mold Temperature | 86.1 - 93.3 | °C | |
| Back Pressure | 0.258 - 0.517 | MPa | |
| Screw Speed | 45 - 55 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 610 - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niuk TPC1008 (General) | Shanghai Niuk New Plastic Technology Co., Ltd. | Acetal (POM) Copolymer | Niuk |
| Baoding 67I74D | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Evermore PUR UP-9330N | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |
| Devcon Ceramic Repair Compound | Devcon | Epoxy | Devcon |
| LTP ZC-1150 GF 40% | Chengdu Letian Plastics Co., Ltd | PPS | LTP |