Plenco 02308 (Injection)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sVDW3x_Plenco-02308-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 02308 is a general purpose organic filled phenolic molding compound, offering improved heat resistance and optimized cure properties. UL recognized under component file E40654. 02308 is available in black or brown color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.32 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8640 | MPa | ASTM D638 |
| Tensile Strength | 58.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 7470 | MPa | ASTM D790 |
| Flexural Strength | 88.0 | MPa | ASTM D790 |
| Compressive Strength | 190 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18.1 | J/m | ASTM D256 |
| Notched Izod Impact | 15 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 141 | °C | ASTM D648 |
| Continuous Use Temperature | 199 | °C | ASTM D794 |
| CLTE - Flow | 5.9E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.4E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 11 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.90 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.053 | ASTM D150 | |
| Arc Resistance | 142 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.33%Heat Resistance, ASTM D794: 199°CDrop Ball Impact, PLENCO Method: 89 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 66.0 - 82.0 | °C | |
| Front Temperature | 82.0 - 99.0 | °C | |
| Processing (Melt) Temp | 104 - 115 | °C | |
| Mold Temperature | 165 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V70SW | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Michilene F8100TL20-03 | API Polymers, Inc. | PP Homopolymer | Michilene |
| ExxonMobil™ LDPE LD 159AC | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Hipolyene 7151 M1 HF | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Sylvin 9077-95LMW White 1457 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |