Generic Nylon, Unspecified
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sUpeik_Generic-Nylon-Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon, Unspecified This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.01 - 1.45 | g/cm³ | ASTM D792 |
| 23°C | 1.02 - 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.6 - 29 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.20 - 3.7 | % | ASTM D955 |
| Transverse flow : 23°C | 0.67 - 2.6 | % | ASTM D955 |
| 23°C | 7.5E-3 - 2.6 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.27 - 1.3 | % | ASTM D570 |
| Saturated, 23°C | 3.3 - 8.6 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.90 - 2.0 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 71 - 118 | ASTM D785 | |
| Durometer Hardness (23°C) | 75 - 82 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 500 - 4240 | MPa | ASTM D638 |
| 23°C | 590 - 3290 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 22.6 - 186 | MPa | ASTM D638 |
| Yield, 23°C | 40.0 - 114 | MPa | ISO 527-2 |
| Fracture, 23°C | 39.0 - 64.9 | MPa | ASTM D638 |
| Fracture, 23°C | 40.0 - 74.0 | MPa | ISO 527-2 |
| 23°C | 50.7 - 69.9 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.5 - 60 | % | ASTM D638 |
| Yield, 23°C | 5.0 - 8.5 | % | ISO 527-2 |
| Fracture, 23°C | 0.70 - 51 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 200 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 50 - 57 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 305 - 12700 | MPa | ASTM D790 |
| 23°C | 275 - 3250 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 50.5 - 153 | MPa | ASTM D790 |
| 23°C | 13.5 - 152 | MPa | ISO 178 |
| Yield, 23°C | 73.6 - 304 | MPa | ASTM D790 |
| Coefficient of Friction | 0.20 - 1.0 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 - 14 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 10 - 130 | J/m | ASTM D256 |
| 23°C | 4.0 - 85 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 117 - 197 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 113 - 161 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.9 - 266 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 59.7 - 147 | °C | ISO 75-2/A |
| Glass Transition Temperature | 140 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 125 - 137 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 198 - 260 | °C | |
| -- | 55.0 - 260 | °C | ISO 11357-3 |
| -- | 190 - 250 | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.9E-5 - 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.9E-5 - 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.22 - 3.8 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+5 - 1.0E+14 | ohms | ASTM D257 |
| -- | 1.0E+11 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 4.0E+8 - 1.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+12 - 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 14 - 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 4.80 | IEC 60250 | |
| Dissipation Factor (23°C) | 0.012 - 0.15 | IEC 60250 | |
| Comparative Tracking Index | 598 - 600 | V | IEC 60112 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 0.60 - 1.1 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 74.6 - 90.1 | °C | |
| Drying Time | 3.9 - 5.2 | hr | |
| Rear Temperature | 265 - 280 | °C | |
| Middle Temperature | 276 - 292 | °C | |
| Front Temperature | 253 - 301 | °C | |
| Processing (Melt) Temp | 246 - 327 | °C | |
| Mold Temperature | 48.9 - 149 | °C | |
| Injection Pressure | 43.8 - 105 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon, UnspecifiedThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 232 - 314 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon, UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9018 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Sumitomo Phenolic FM 4005X4649 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| Axiall PVC 8642 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| COSMOTHENE® F410-7 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® |
| Hanwha Total PP TH52 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |