Lumid® GP2430B(W)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sUn82Q_Lumid-GP2430B-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose Applications Automotive(Air Intake Manifold) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 6.40 mm) | 216 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 6.40 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 12700 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 30.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 260 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 255 | °C | |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 4.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 285 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure 5 | 0.981 to 2.94 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AMVO TLD | Arkema | Nylon 12 | Rilsamid® |
| Sicoklar UG81 | Ravago Group | PC | Sicoklar |
| Kumho SAN SAN 350HW | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |
| PermaStat PLUS® 300 A | RTP Company | PC | PermaStat PLUS® |
| ESTOPLAST ZK 6002BB02 | Ester Industries Ltd. | PC | ESTOPLAST ZK |